In order to make the valve has the strength of the metal, and has the property of corrosion resistance, the company selects the cast steel, stainless steel, gray cast iron shell, shell lumen is medium flow components is good corrosion resistant engineering plastics as lining material, USES the advanced steel lining plastic moulding technology, according to the specifications of the valve and use the medium size, can choose the thickness of the lining is 3 ~ 8 mm fluorine plastic (F46, F4, PFA, PVDF), polypropylene (PP), polyethylene (PE), olefin copolymer (PO) as the lining materials, such as teflon is chosen as the filler sealing ring. Each valve passes the inspection edm and hydrostatic test. All kinds of steel lining plastic valves are opening and closing flexible, reliable sealing performance, all kinds of acid, alkali corrosion resistant performance is good, long life and other advantages.
1, FEP FEP (F46)
Applicable medium: any organic solvents or reagent, the concentration of acid, alkali, salt, alcohol, acetone solution (except the fluorine element with high temperature, molten alkali and chlorine trifluoride reaction, are not corroded when in contact with other chemicals). Working temperature 150 ℃ or less.
Features: F46 resin mechanics, electricity performance and chemical stability, basically similar to those of ptfe, but outstanding advantage is high impact toughness, even sample of band gap continuously and has excellent weather resistance and radiation, easy processing, in addition, the use of temperature is lower than the F4 other performance to keep the good performance of F4, thus making it instead of the teflon material.
2, PTFE teflon (F4)
Applicable medium: any organic solvents or reagent, the concentration of acid, alkali, salt, alcohol, acetone solution (except the fluorine element with high temperature, molten alkali and chlorine trifluoride reaction, are not corroded when in contact with other chemicals). Working temperature 180 ℃ or less.
Features: F4 resin because of the particularity of the molecular chain of chemical structure, make its have strong corrosion resistance and high temperature resistance, but the shortage of the ptfe has the processing difficulties, production process, the scrap rate is higher, so the cost of processing than F46.
3, soluble ptfe (PFA)
Applicable medium: any organic solvents or reagent, the concentration of acid, alkali, salt, alcohol, acetone solution (except the fluorine element with high temperature, molten alkali and chlorine trifluoride reaction, are not corroded when in contact with other chemicals). Working temperature 180 ℃ or less.
Characteristic: the PFA resins in order to overcome the shortage of ptfe processing molding difficult, and the development of a new species, completely keep the good performance of the F4. Good mechanical and electrical insulating properties, the biggest advantage is easy to processing molding, making it a instead of the teflon material.
4, reinforced polypropylene (FRPP)
Applicable medium: aqueous solution of inorganic salts, inorganic acid, alkali of thin or thick solution. Working temperature of 100 ℃ or less.
Features: is one of the most light plastic, and its yield strength, tensile strength and compression strength are better than polyethylene, have outstanding rigidity, heat resistance, easy forming, etc. Impact, liquidity is improved after modification.
5, polyolefin (PO)
Applicable medium: some organic solvents and reagents, a dilute acid solution, alkali, salt and so on. Working temperature 100 ℃ or less.
PO has good corrosion resistance and processing performance, widely used for anti-corrosion of all kinds of roll forming equipment, also used in moulding lining valves.
The user can choose different lining material according to the working condition, temperature
Number |
Type |
Drive way |
The connection method |
Structure form |
The lining material |
Nominal pressure |
The valve body material |
1 |
Q ball valve |
Manual 3 turbine 6 pneumatic 9 electric |
4 flange connection 7 for clip |
1 vertical plate (middle) |
F4-PTFE F46-FEP PP polypropylene PO polyolefin PE polyethylene |
Using MPa 10 times the value of said |
C-WCB P-CF8 PL-CF3 RL-CF3M |
2 |
D butterfly valve |
1 straight through |
|||||
3 |
J cut-off valve |
1 through 4 right Angle type 5 once-through |
|||||
4 |
G the diaphragm valve |
1 weir 5 right Angle |
|||||
5 |
Z gate valves |
1 straight through |
|||||
6 |
H the check valve |
1 lift straight through |
|||||
2 lift vertical |
|||||||
4 swing |
Design and manufacture of HG/T 3704-3704
Flange dimensions GB9112 ~ GB9131-2000 "steel pipe flange national standard assembly"
Structure length GB1221-89 "the length of flange connection structure of metal valve"
Inspection and testing of GB/T13927-92 "the common valve pressure test"
Name |
Kg pressure |
Test pressure(MPa) |
Pressure of work (MPa) |
Test of time(S) |
Eligibility criteria |
|
Shell strength |
Sealing pressure |
|||||
Ball valve |
1.0/1.6 |
1.5/2.5 |
1.1/1.76 |
1.0/1.6 |
60 |
Zero leakage |
Globe valve |
1.6/2.5 |
2.5/3.75 |
1.76/2.75 |
1.6/2.5 |
||
Right Angle valve |
||||||
Dc valve |
||||||
The check valve |
1.6 |
2.5 |
1.76 |
1.6 |
||
The diaphragm valve |
0.6 |
0.9 |
0.66 |
0.6 |
||
Butterfly valve |
1.0/1.6 |
1.5/2.5 |
1.1/1.76 |
1.0/1.6 |
||
Feeding valve |
1.0/1.6 |
1.5/2.5 |
1.1/1.76 |
1.0/1.6 |
||
Gate valves |
1.6 |
2.5 |
1.76 |
1.6 |
||
Spark test |
Electric spark tester, 10-12 kv voltage probe 50 ㎜ / s uniform scanning speed along the lining surface, there is no white spark |
s
w
e
e
p